Ceilcote® 2000 is a high performance, flake filled epoxy novolac coating that is designed to provide maximum resistance to 98% sulphuric acid.
Intended Uses
For use on structural steel exposed to chemical spillage, concrete floors and chemical trenches in process areas, chemical pump pedestals and areas which may be exposed to repeated chemical spillage or fumes.
Ceilcote 2000 Flakeline is employed in many applications in the chemical processing and mining market sectors, where resistance to high concentrations of acid are required.
| Colour | Grey, Tile Red |
| Gloss Level | Not applicable |
| Volume Solids | 100% |
| Typical Thickness | 375-625 microns (15-25 mils) dry equivalent to 375-625 microns (15-25 mils) wet per coat |
| Theoretical Coverage | 2 m²/litre at 500 microns d.f.t and stated volume solids |
| Practical Coverage | Allow appropriate loss factors Coverage will vary according to individual systems and the configuration of the surface to be coated; consult the relevant Application Guidelines and specification for further information. |
| Method of Application | Airless Spray, Roller, Brush |
| Regulatory Data | |
| Flash Point | Part A 126 °C Part B 109 °C Mixed >100 °C |
| Product Weight | 1.23 kg/l (10.3 lb/gal) |
| VOC-EU | 36 g/kg¹ |
¹ EU Solvent Emissions Directive (Council Directive 1999/13/EC)
| Surface Temperature | 10 °C | 15 °C | 25 °C | 40 °C |
| Touch Dry | 24 hrs | 18 hrs | 3 hrs | 1.5 hrs |
| Hard Dry | 24 hrs | 18 hrs | 6 hrs | 3 hrs |
| Overcoating Interval, Minimum | 12 hrs | 10 hrs | 6 hrs | 2 hrs |
Surface Preparation
All surfaces to be coated should be clean, dry and free from contamination. Prior to paint application all surfaces should be assessed and treated in accordance with ISO 8504:2000.
Oil or grease should be removed in accordance with SSPC-SP1 Solvent Cleaning.
Steel Substrates:
For immersion service or service in humid conditions or elevated temperatures, this product should be applied to surfaces which have been prepared by abrasive blast cleaning to Sa3 (ISO 8501-1:2007), SSPC SP5 or NACE #1. For dry environments, abrasive blast cleaning to Sa2½ (ISO 8501-1:2007), SSPC SP10 or NACE #2 will be suitable. A sharp, angular surface profile of 75-100 microns (3-4 mils) is required.
Concrete Substrates:
Ceilcote 2000 Flakeline is also suitable for application to concrete in certain conditions; please see Product Application Guidelines for further information.
| Mixing | Ceilcote 2000 Flakeline must always be mixed and applied in accordance with the detailed Application Guidelines for the subsequent system. Material is supplied in two containers as a unit. Always mix a complete unit in the proportions supplied. Once the unit has been mixed it must be used within the working pot life specified. Material is supplied in two containers as a unit. Always mix a complete unit in the proportions supplied. Once the unit has been mixed it must be used within the working pot life specified. (1) Agitate Base (Part A) with a power agitator. (2) Combine entire contents of Curing Agent (Part B) with Base(Part A) and mix thoroughly with power agitator. |
| Mix Ratio | Always mix full units. |
| Working Pot Life | 10 °C - 45 mins 15 °C - 35 mins 25 °C - 25 mins 40 °C - 20 mins |
| Airless Spray | Recommended Tip Range 0.58-0.68 mm (23-27 thou) Total output fluid pressure at spray tip not less than 247 kg/cm² (3512 p.s.i.) |
| Brush | Suitable - Touch up and small areas only Multiple coats may be required to achieve specified film thickness |
| Roller | Suitable Multiple coats may be required to achieve specified film thickness |
| Thinner | Not suitable. Do not thin. |
| Cleaner | Ceilcote T-410 Solvent International GTA203 |
| Work Stoppages | Do not allow material to remain in hoses, gun or spray equipment. Thoroughly flush all equipment with Ceilcote T-410 Solvent or International GTA203. Once units of paint have been mixed they should not be resealed and it is advised that after prolonged stoppages work recommences with freshly mixed units. |
| Clean Up | Clean all equipment immediately after use with Ceilcote T-410 Solvent or International GTA203. It is good working practice to periodically flush out spray equipment during the course of the working day. Frequency of cleaning will depend upon amount sprayed, temperature and elapsed time, including any delays. All surplus materials and empty containers should be disposed of in accordance with appropriate regional regulations/legislation. |
Product Characteristics
The detailed Application Guidelines for the relevant Ceilcote system should always be consulted prior to use.
The exact specification with regards to dry film thickness and number of coats will be provided by International Protective Coatings prior to application start up.
Surface temperature must always be a minimum of 3°C (5°F) above dew point. Ensure adequate ventilation is provided throughout application and curing. Dehumidification (DH), air conditioning and/or heating equipment may be necessary to control environmental conditions.
This product can be susceptible to amine blush; if present, wash with water and allow to dry before overcoating.
Relative humidity should be <85 %.
When working outside or in direct sunlight, concrete "gassing" or "breathing" may occur when the surface temperature is rising due to sunlight or increasing ambient temperature. This can cause bubbles or holes in the applied floor, lining or coating. When this problem occurs it is necessary to shade the surface from sunlight and/or apply the material in the cooler evening or at night so that initial cure can take place without air escaping from the concrete. Consult International Protective Coatings for more detailed recommendation.
Ceilcote 2000 Flakeline may be returned to service (for concentrated sulphuric acid immersion service) after the following intervals:
• 20 °C (70 °F): 7 days
• 35 ° C (90 °F): 3 days
However, for immersion service in sulphuric acid at concentrations of 90% or higher, Ceilcote 2000 Flakeline must be post-cured for 6-8 hours at 70ºC (158ºF). Some discolouration of the product may occur. For exposure to 98% sulphuric acid, temperature must not exceed 40ºC (104ºF).
Ceilcote 2000 Flakeline is not intended to be used as a cosmetic finish and colour stability will not be achievable.
Maximum continuous dry temperature resistance for Ceilcote 2000 Flakeline is 120°C (248°F).
Note:
VOC values are typical and are provided for guidance purpose only. These may be subject to variation depending on factors such as differences in colour and normal manufacturing tolerances.
Low molecular weight reactive additives, which will form part of the film during normal ambient cure conditions, will also affect VOC values determined using EPA Method 24.
Systems Compatibility
Ceilcote 2000 Flakeline should be applied to correctly prepared substrates. However, it is suitable for application to the following primers:
• Ceilcote 680M
Ceilcote 2000 Flakeline may also form a constituent part of other systems such as:
• Ceilcote 2000 Ceilline
• Ceilcote 2000MR
Ceilcote 2000 Flakeline should only be overcoated with itself.
Additional Information
Further information regarding industry standards, terms and abbreviations used in this data sheet can be found in the documents available at www.international-pc.com:
• Definitions & Abbreviations
• Surface Preparation
• Paint Application
• Theoretical & Practical Coverage
• Ceilcote 2000 Flakeline Application Guidelines
Safety Precautions
This product is intended for use only by professional applicators in industrial situations.All work involving the application and use of this product should be performed in compliance with all relevant national Health, Safety and Environmental standards, regulations and legislation.
Proper ventilation must be provided during application and afterwards during curing (refer to product datasheets for typical curing times) to ensure safe limits and prevent fires and explosions. Forced extraction will be required in confined spaces. Ventilation and/or respiratory personal protective equipment (airfed hoods or appropriate cartridge masks) must be provided during application and curing. Take precautions to avoid skin and eye contact (overalls, gloves, goggles, masks, barrier cream, etc).
Before use, obtain, read and then follow the advice given on the Material Safety Data Sheets (Parts A and B if two-pack) and the Health and Safety section of the Coatings Applications Procedures for this product.
In the event that welding or flame cutting is performed on metal coated with this product, dust and fumes will be emitted which will require the use of appropriate personal protective equipment and adequate local exhaust ventilation.
The detailed safety measures are dependent on application methods and the work environment. If you do not fully understand these warnings and instructions or if you cannot strictly comply with them, do not use the product and consult International Protective Coatings.
| Volume (Liters) | Pack Sizes (Liters) | |
| Ceilcote® 2000 Flakeline Part A | 15.6 | 20 |
| Ceilcote® 2000 Flakeline Part B | 4.4 | 5 |
Storage
Lifetime at 25 °C
Minimum 12 Month(s)
Subject to re-inspection thereafter. Store in dry, shaded conditions away from sources of heat and ignition.
Diese Angaben stammen aus dem offiziellen Technischen Datenblatt von dem Lackhersteller. Wir übernehmen keine Gewährleistung für die Richtigkeit / fehlerhafte Angaben.
Wir bitten Sie, sich ausschließlich ans Technische Datenblatt des Herstellers zu halten, welches Sie weiter unten als PDF-Download finden.
All information were taken out of the Technical Data Sheet provided by the manufacturer. We don't garantuee the correctness of any information.
Please adhere solely to the Technical Data Sheet provided by the manufacturer which you can download as a PDF-File further below.